  • Permanently elastic sealant
  • Not yellowing
  • Paintable
  • Can be used as mirror adhesive
  • Eco friendly

Packaging: 12 units.

Add to cart

Universal, highly adhesive 1-component sealant based on MS-hybrid-polymer for indoor and outdoor application, on absorbent and non absorbent substrates.

Absolutely weatherproof, moisture curing, silicone free, neutral polymerization, odorless, with low emissions.

Connection joints on concrete, metals, wood and various plastics. For joint sealing in structural engineering, outside of DIN 18540.

Various adhesions in construction and industry.


The precondition for maximum adhesive strength is a clean, fat free surface with a perfect structure. Turbo MS adheres to many substrates as lacquered wood, metals and various plastics without Adhesion promoter.

Cleaning of the surface
The substrate must be stable, clean, dust-, oil- and fat-free. Good results can be achieved with rubbing alcohol.

Adhesion promoter
On many clean substrates a good adherence can be achieved without Adhesion promoter. However, it should always be tested, if the cured product is exposed to big fluctuations in temperature or has contact with water. In this case or on difficult, absorbent substrates we recommend the application of Adhesion promoter V21. The Adhesion promoter V2 is recommended for non absorbent substrates.

We recommend tooling the joints with tooling solvent and eventually using help-tools for joints.

Work and environment safety
Important information on the work and environment security you can find in the safety data sheet.

Chemical resistance

  • good to water, aliphatic solvents, oils, greases, diluted inorganic acids and alkalis
  • moderate to esters, ketones and aromatics
  • not resistant to concentrated acids and chlorinated hydrocarbons
  • completely weather-resistant

Turbo MS Economy is paintable
Because of the diversity of varnishes and paints on the market, we recommend a preliminary test. Using paints based on alkyd resins the drying process may be hold up.
If Turbo MS is used for painted or plastered substrates, you have to keep an enough long drying time (normally 10 days).
After cleaning with acetone, joints can be varnished at any time.


Shore-A-hardness (DIN 53505)              36
after 3 weeks of storage

Modulus elongation at 100%                  ≤ 0.7 N/mm2
DIN 53504 S2
Storage during 7 days

Elongation at break (DIN 53504 S2)      ≥ 500 %
Storage during 7 days

Tensile strength (DIN 53504 S2)            ≥ 1.3 N/mm2
Storage during 7 days

Movement capability                              <20 %

Consistency                                          ≤ 3 mm

Tooling time                                          max. 30 min.

Curing through                                     after 24 h: ≥ 2.5 mm
                                                           after 48 h: ≥ 3.5 mm

Density                                                1.54 ± 0.05 g/cm3

Change of volume                                ≤ 3 %
(DIN EN ISO 10563)

Temperature resistance                      -40 °C to + 90 °C
3.Application temperature                    +5 °C to + 40 °C
Temperature of the substrate               +5 °C to + 40 °C

Shelf life                                             18 months from production date
Storage conditions                               cool and dry

All measurements were performed under normal conditions (+23°C and 50% relative humidity).