€ 15.63 *
* Price (VAT included)

  • Novel, innovative adhesive and sealant based on SMP-Polymer
  • Free of isocyanate, solvents and silicone
  • Moisture curing
  • Neutral polymerization
  • Odourless
  • With a low density which can be applied where at the same time by bonding or adhering a warmth- or coldness
    isolation as well as reduction of sound and/or vibration shall be achieved
  • Weight saving
  • Suitable for compression joints

Add to cart

MS Isolation is a novel, innovative sealant based on SMP-Polymer.

MS Isolation is free of isocyanate, solvents and silicone, is moisture curing, neutral polymerization, odourless MS Isolation is an adhesive and sealant with a low density which can be applied where at the same time by bonding or adhering a warmth- or coldness isolation as well as reduction of sound and/or vibration shall be achieved.

Due to the extraordinary low density of 0.38 g/cm3 a significant weight saving can be realised. Because of the compression the product is suitable for compression joints.

 

 

    • Filling of local separation at frames for windows and doors
    • Filling of cracks and holes in walls
    • Bonding of isolation material
    • Isolation of connections in bathrooms (e.g. connection bathtub – wall,…)
    • Sealing and isolation of local separation in floor underlayment
    • Easy sealing or bonding inside of car bodies
    • Steaming of vibrating elements (ventilation area, automobile body,...)
    • Weight saving due to the low density
    • Acoustic baffle of inner area and at the same time isolation of warmth and coldness

Ideal for frames for windows and doors, cracks and holes in walls, bonding of isolation material, isolation of connections in bathrooms (e.g. connection bathtub – wall,…).

Handling
MS Isolation can be applied in stripe peels off the sausage by hand or compressed air pistol. Alternatively an automatic handling of hobbocks or drums is possible. MS Isolation is applicable by spatula. Hollow spaces can easily be closed.

Surface cleaning
To achieve best results the substrate has to be prepared according to the best available technology. The substrate has to be on hand in defined, stable consistency. All undefined surfaces have to be removed by appropriate treatment; MS ISOLATION has to be applied promptly on the prepared area.

Adhesion promoter
A good adherence is achieved on many clean substrates without adhesion promoter.
If the cured product is exposed to big fluctuations in temperature or has contact with water we recommend the application of Adhesion Promoter V40 on non absorbent substrates and Adhesion Promoter V21 on absorbent substrates. Thermo or powder-coated surfaces should be treated previously with Adhesion Promoter V40. The adhesion on specific synthetically surfaces can be improved by usage of Adhesion Promoter V30.

Work and environment safety
Important information on the work and environment security you can find in the safety data sheet.

Chemical resistance

  • good to water, aliphatic solvents, oils, greases, diluted inorganic acids and alkalis
  • moderate to esters, ketones and aromatics
  • not resistant to concentrated acids and chlorinated hydrocarbons

MS Isolation is paintable.
Because of the diversity of varnishes and paints on the market, we recommend a preliminary test. Using paints based
on alkyd resins the drying process may be hold up.

Shore-A-hardness, DIN 53505                             32

Modulus elongation at 100%,                               ≤ 0.8 N/mm²
DIN 53504 S2

Elongation at break, DIN 53504 S2                      ≥ 100%

Tensile strength, DIN 53504 S2                           ≥ 1.0 N/mm²

Consistency                                                       stable

Tooling time                                                       max. 15 min.

Capacity of heat conduction                                 0.063 W7mk

Curing rate                                                        after 24h ≥ 3.5 mm

Curing rate                                                        after 48h ≥ 5.5 mm

Density                                                              0.38 ± 0.05 g/cm³

Volume change, DIN EN ISO 10563                      approx. 5%

Temperature resistance after curing                     - 40 °C to + 80 °C

Application temperature                                      + 5 °C to + 40 °C

All measurements were performed under normal conditions (23 °C and 50 % relative humidity).